VALOX™ SHF4910 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ynpGZt_VALOX-SHF4910-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 6.5% glass reinforced, Super High Flow, flame retardant PBT. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 31 | g/10 min | ASTM D1238, ISO 1133 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 25.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.70 to 1.3 | % | |
| Flow : 3.20 mm | 0.70 to 1.3 | % | |
| Across Flow 2 | 1.1 to 1.7 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.26 | % | |
| Equilibrium, 23°C, 50% RH | 0.070 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 4210 | MPa | ASTM D638 |
| -- | 4350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 4 | 66.0 | MPa | ASTM D638 |
| Yield | 73.0 | MPa | ISO 527-2/5 |
| Break 5 | 66.0 | MPa | ASTM D638 |
| Break | 73.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 6 | 3.1 | % | ASTM D638 |
| Yield | 3.5 | % | ISO 527-2/5 |
| Break 7 | 3.1 | % | ASTM D638 |
| Break | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 8 | 3650 | MPa | ASTM D790 |
| -- 9 | 3650 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 115 | MPa | ISO 178 |
| Yield, 50.0 mm Span 10 | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C | 5.0 | kJ/m² | ISO 179/2C |
| 23°C 11 | 5.0 | kJ/m² | ISO 179/1eA, ISO 179/2C |
| Charpy Unnotched Impact Strength | ISO 179/2U | ||
| -30°C | 27 | kJ/m² | |
| 23°C | 32 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 36 | J/m | ASTM D256 |
| 23°C | 42 | J/m | ASTM D256 |
| -30°C 12 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 13 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 320 | J/m | ASTM D4812 |
| 23°C | 490 | J/m | ASTM D4812 |
| -30°C 14 | 21 | kJ/m² | ISO 180/1U |
| 23°C 15 | 26 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 48.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 200 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 160 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 16 | 145 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 216 | °C | ASTM D1525 17 |
| -- | 191 | °C | ASTM D1525 18 |
| -- | 217 | °C | ISO 306/A50 |
| -- | 192 | °C | ISO 306/B50 |
| -- | 195 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 5.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 6.3E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 0.800 mm, in Oil | 51 | kV/mm | |
| 1.60 mm, in Oil | 31 | kV/mm | |
| 3.20 mm, in Oil | 18 | kV/mm | |
| Dissipation Factor (1 MHz) | 0.016 | IEC 60250 | |
| Comparative Tracking Index | 275 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 28 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (250°C, 1500 sec^-1) | 110 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 245 | °C | |
| Middle Temperature | 240 to 255 | °C | |
| Front Temperature | 245 to 265 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Tensile Bar |
| 3 . | 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | Type I, 5.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 mm |
| 17 . | Rate A (50°C/h), Loading 2 (50 N) |
| 18 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fluoroplex I 10 - GML | UNIFLON | PTFE | Fluoroplex |
| Haysite Plastics H722 GPO-1 | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| Karina RED PVC COMPOUND 701D42/266-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POFEX 8200EP90M | POLYROCKS CHEMICAL CO., LTD | TPE | POFEX |
| Sylvin 2999-67LG Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |