Lupol® HI5302S
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yndB9x_Lupol-HI5302S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUPOL HI-5302S is reinforced with combination of glass-fiber and inorganic filler, this product is excellent in dimensional stability and distortion-resistant characteristics. HI-5302S is ideal for relatively long shape products and those demanding dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.0 to 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 25.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 2260 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 41.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 78.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 210 to 230 | °C | |
| Nozzle Temperature | 210 to 240 | °C | |
| Melt Temperature (Aim) | 210 | °C | |
| Mold Temperature | 40.0 to 90.0 | °C | |
| Injection Pressure | 29.4 to 118 | MPa | |
| Holding Pressure | 78.5 to 98.1 | MPa | |
| Back Pressure | 0.490 to 3.92 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC GN1009FM | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Sylvin 9812-80 Black | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Vipel® F764-BBD-00 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Nypol® PA A3 HF PRT0327 NR440 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Adsyl 7572 XCP | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |