MALECCA K-700
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | MALECCA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ynbPTf_MALECCA-K-700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MALECCA K-700 is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. |
| General Information | |
|---|---|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.09 | g/cm³ | ASTM D792 |
| 23°C | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/10.0 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.80 to 1.0 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 120 | ASTM D785 | |
| R-Scale | 112 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 39.0 | MPa | ASTM D638 |
| -- | 1900 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 37.0 | MPa | |
| Break | 37.0 | MPa | |
| Nominal Tensile Strain at Break | 11 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 1850 | MPa | ASTM D790 |
| -- 3 | 1900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 63.0 | MPa | ASTM D790 |
| -- 5 | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed 6 | 138 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 126 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ASTM D1525 7 |
| -- | 150 | °C | ISO 306/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 230 to 260 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Nozzle Temperature | 240 to 265 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.490 to 0.981 | MPa | |
| Screw Speed | 50 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 15 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 15 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Edgewise |
| 7 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7430 GF 10 GK 20 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Ultramid® A3EG7 | BASF Corporation | Nylon 66 | Ultramid® |
| NYCOA Polyamide 2062 | Nycoa (Nylon Corporation of America) | Nylon 66/6 | NYCOA Polyamide |
| Nypol® PA A3 G30 HL CNZA178 NR466 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| BMC HT12-1024 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |