Romiloy®4010 is an acrylonitrile butadiene styrene nylon (ABS nylon) material,. This product is available in Europe, and the processing method is injection molding. Romiloy®The main features of the 4010 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 1.0 - 1.4 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1750 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 42.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 200 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1500 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 25 | kJ/m² | ISO 179/1eA |
| 23°C | 85 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 140 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with DIN 16901.Tensile Strain @ Break, DIN EN ISO 527, 50 mm/min, 23°C: >200% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 50.0 - 90.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 1.00 | MPa | |
| Screw Speed | 12 - 18 | rpm |
| Injection instructions |
|---|
| Holding Pressure: moderate to high |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Weatherflex™ CS1536WX NTL70B | Colorite Polymers | PVC, Flexible | Weatherflex™ |
| BioCeres® BC-LBI01 | FuturaMat | Biodeg Polymers | BioCeres® |
| Altuglas® DRT | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| Karina WHITE PVC COMPOUND -E 803-10/ 1-A-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KOPPS® S13G40BL | Kolon Plastics, Inc. | PPS | KOPPS® |