| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | POPELEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ynP2BL_POPELEN-V-235N.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| Flame Retardant, Heat Resistance |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 32.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 2940 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -10°C | 20 | J/m | |
| 23°C | 29 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 135 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TFE 5 HS | RTP Company | Nylon 66 | RTP |
| DOMAMID® 66G35V0P 1001 | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Eastar™ MN006 Natural | Eastman Chemical Company | Copolyester | Eastar™ |
| LOTTMER HX-080AB | Lotte Chemical Corporation | TPE | LOTTMER |
| TECHNYL® B 738 MX15 GREY 3279 | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |