MAJORIS GFR320
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ylOBf1_MAJORIS-GFR320.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GFR320 is a 30% chemically coupled glass fibre reinforced polypropylene compound, halogen flame retardant UL 94 V0 with high LOI, intended for injection moulding. The product is available in natural (GFR320) but other colours can be supplied on request. GFR320 has a high flow rate and good dimensional stability. APPLICATIONS GFR320 is intended for the injection moulding for the automotive applications and electrical components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 21 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.50 - 0.60 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 80.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 2.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 8000 | MPa | ISO 178 |
| Flexural Stress 2 | 138 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 37 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 147 | °C | ISO 75-2/A |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 375 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | IEC 60695-2-12 |
| 2.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 29 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 250 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PC 1005 GF 10 FL | TER HELL PLASTIC GMBH | PC | TEREZ PC |
| Desmovit® DP LFC 9585 | geba Kunststoffcompounds GmbH | TPU-Ester/Ether | Desmovit® |
| Fiberfil® J-69/20/E | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Hostacom D1179 0907 | LyondellBasell Industries | PP Impact Copolymer | Hostacom |
| INNOPOL® PP CS 1-5830 SA | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |