MAGNUM™ 275
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yi5yLe_MAGNUM-275.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAGNUM™ 275 ABS resin is a low gloss, low flow ABS resin with good impact. MAGNUM ABS resins are thermoplastic materials that provide an excellent balance of processability, impact resistance, and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resins are available in a wide range of melt flow rates, impact strengths, and heat resistances for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion, and thermoforming. MAGNUM ABS resins offer a wide range of processing abilities and impact resistance for low gloss injection molding applications. Combined with heat resistance, tensile and flexural strength, MAGNUM ABS resins are used in a wide variety of injection molding applications. Applications
Complies with:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| -- | 1050 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.6 | g/10 min | ASTM D1238 |
| Melt volume-flow rate (220°C/10.0 kg) | 9.00 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 1830 | MPa | ASTM D638 |
| -- | 2000 | MPa | ISO 527-2 4 |
| Tensile Strength | |||
| Yield 5 | 37.2 | MPa | ASTM D638 |
| Yield | 44.0 | MPa | ISO 527-2 6 |
| Break 7 | 34.5 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield 8 | 3.0 | % | ASTM D638 |
| Yield | 2.6 | % | ISO 527-2 9 |
| Break 10 | 100 | % | ASTM D638 |
| Nominal strain at break | 30 | % | ISO 527-2 11 |
| Flexural Modulus 12 | 2030 | MPa | ASTM D790 |
| Flexural Strength 13 | 63.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 14 | ||
| -30°C | 9.00 | kJ/m² | |
| 23°C | 22.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 15 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact 16 | ASTM D256 | ||
| -18°C, 3.20 mm | 130 | J/m | |
| 23°C, 3.20 mm | 270 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -18°C, Peak Energy | 32.8 | J | |
| -18°C, 3.20 mm, Total Energy 17 | 37.3 | J | |
| 23°C, Peak Energy | 32.8 | J | |
| 23°C, 3.20 mm, Total Energy 18 | 46.3 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 93.3 | °C | ASTM D648 |
| 0.45 MPa | 95.0 | °C | ISO 75-2 19 |
| 1.8 MPa, Unannealed, 3.20 mm | 79.4 | °C | ASTM D648 |
| 1.8 MPa | 85.0 | °C | ISO 75-2 20 |
| Vicat Softening Temperature | |||
| -- | 107 | °C | ASTM D1525 |
| 50°C/h, B (50N) | 99.0 | °C | ISO 306 21 |
| CLTE - Flow | 7.9E-5 | cm/cm/°C | ISO 11359-2 22 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 23(1.52 mm) | HB | UL 94 | |
| Burning Behav. at 1.6mm nom. thickn. (1.47 mm, UL) | HB | ISO 1210 24 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 1000 mm/min |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Type I, 51 mm/min |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Type I, 51 mm/min |
| 8 . | Type I, 51 mm/min |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Type I, 51 mm/min |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Type I, 2000 mm/min |
| 13 . | Type I, 2000 mm/min |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | 0.25 mm Notch Depth |
| 17 . | 3.39 m/sec |
| 18 . | 3.39 m/sec |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 22 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 23 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 24 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ XLT65 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| UBE Nylon 5034 UC2 | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| VAMPAMID 6 3026 V0 DF | Vamp Tech | Nylon 6 | VAMPAMID |
| LNP™ THERMOCOMP™ DX15354 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |
| THERMOLAST® K TF6ADN (Series: FC/AD1/PS) | KRAIBURG TPE | TPE | THERMOLAST® K |