Plaslube® PBT GB30 TL15
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yhyYc9_Plaslube-PBT-GB30-TL15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube® PBT GB30 TL15 is a Polybutylene Terephthalate (PBT) product filled with 30% glass bead. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.6 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 47.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 4000 | MPa | ASTM D790 |
| Flexural Strength | 81.4 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.23 | ||
| vs. Steel - Static | 0.18 | ||
| Wear Factor | 50 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 133 | °C | ASTM D648 |
| CLTE - Flow | 3.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 16 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 232 to 274 | °C | |
| Middle Temperature | 232 to 274 | °C | |
| Front Temperature | 232 to 274 | °C | |
| Processing (Melt) Temp | 232 to 246 | °C | |
| Mold Temperature | 65.6 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ F113G | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| Quadrathane™ ALC-93A-B30 | Biomerics, LLC | TPU-PC | Quadrathane™ |
| Romiloy® 1035/07 GF10 | ROMIRA GmbH | PC+ABS | Romiloy® |
| Sumiliteresin® PR-51820 | SBHPP | Phenolic | Sumiliteresin® |
| LNP™ THERMOCOMP™ LF002 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |