Drystar™ 0601
| Category: | Copolyester , Copolyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Drystar™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ygnMS7_Drystar-0601.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eastman is pleased to announce the launch of DRYSTAR* copolyesters. This new product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman?s copolyesters are highly valued for their excellent balance of properties such as superior aesthetics, impact strength, and chemical resistance. These properties can be optimally realized when the resins are properly dehydrated in accordance to recommended drying conditions and equipment. Recognizing this value, Eastman conceived Drystar™ copolyesters to allow converters with limited access to desiccant dryers to achieve these optimizations. In addition, some converters with desiccant dryers may still find Drystar™ copolyesters value-adding to attain production flexibility and cost saving by removing the drying process prior to injection molding, profile extruding, or extrusion blow molding copolyesters. The initial launch comprises of the commercialization of four grades of Drystar™ copolyesters and Eastman has on-going program to extend this strategic product-line in the future. *DRYSTAR is only available in the Asia Pacific Region. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.27 | g/cm³ | ASTM D792, ASTM D1505 |
| 23°C | 1.27 | g/cm³ | ISO 1183/D |
| Water Absorption (23°C, 24 hr) | 0.13 | % | ASTM D570, ISO 62 |
| Inherent Viscosity 1 | Internal Method | ||
| Film : 23°C | 0.70 | ||
| Pellets : 23°C | 0.75 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Resistance | ASTM D2582 | ||
| M.D. : 23°C | 93 | N | |
| T.D. : 23°C | 93 | N |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Carbon Dioxide Permeability (23°C) 2 | 49 | cm³·mm/m²/atm/24 hr | ASTM D1434 |
| Tear Propagation Resistance 3 | ASTM D1938 | ||
| M.D. : 23°C | 36 | kN/m | |
| T.D. : 23°C | 36 | kN/m |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, 23°C | 106 | ASTM D785 | |
| R-Scale, 23°C | 109 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield, 23°C | 50.0 | MPa | |
| Break, 23°C | 28.0 | MPa | |
| Tensile Elongation | |||
| Break, 23°C | 130 | % | ASTM D638 |
| Break, 23°C | 100 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2100 | MPa | ASTM D790 |
| 23°C | 2000 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 68.0 | MPa | ISO 178 |
| Yield, 23°C | 70.0 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 250 | µm | |
| Secant Modulus | ASTM D882 | ||
| MD | 1900 | MPa | |
| TD | 1900 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 52.0 | MPa | |
| TD : Yield | 52.0 | MPa | |
| MD : Break | 59.0 | MPa | |
| TD : Break | 55.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield | 4.0 | % | |
| TD : Yield | 4.0 | % | |
| MD : Break | 400 | % | |
| TD : Break | 400 | % | |
| Dart Drop Impact 4 | ASTM D1709A | ||
| -18°C | 500 | g | |
| 23°C | 400 | g | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 1400 | g | |
| TD | 1700 | g | |
| Trouser Tear Resistance 5 | ISO 6383-1 | ||
| MD | 36.0 | N/mm | |
| TD | 36.0 | N/mm | |
| Oxygen Permeability (23°C) | 10 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (38°C, 100% RH) | 7.0 | g/m²/24 hr | ASTM F1249 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 37 | J/m | ASTM D256 |
| 23°C | 100 | J/m | ASTM D256 |
| -40°C | 4.2 | kJ/m² | ISO 180/1A |
| 23°C | 6.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -40°C, 3.20 mm | No Break | ASTM D4812 | |
| -30°C, 3.20 mm | No Break | ASTM D4812 | |
| -20°C, 3.20 mm | No Break | ASTM D4812 | |
| 23°C, 3.20 mm | No Break | ASTM D4812 | |
| -40°C 6 | No Break | ISO 180/1U | |
| -30°C 7 | No Break | ISO 180/1U | |
| -20°C 8 | No Break | ISO 180/1U | |
| 23°C 9 | No Break | ISO 180/1U | |
| Instrumented Dart Impact | |||
| -40°C, 2.50 mm, Energy at Peak Load | 41.0 | J | ASTM D3763 |
| -40°C, 3.20 mm, Energy at Peak Load | 50.0 | J | ASTM D3763 |
| 23°C, 2.50 mm, Energy at Peak Load | 28.0 | J | ASTM D3763 |
| 23°C, 3.20 mm, Energy at Peak Load | 33.0 | J | ASTM D3763 |
| -40°C, 2.50 mm, Energy to Peak Force | 35.0 | J | ISO 6603-2 |
| -40°C, 3.20 mm, Energy to Peak Force | 36.0 | J | ISO 6603-2 |
| 23°C, 2.50 mm, Energy to Peak Force | 40.0 | J | ISO 6603-2 |
| 23°C, 3.20 mm, Energy to Peak Force | 44.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 70.0 | °C | |
| 1.8 MPa, Unannealed | 64.0 | °C | |
| Glass Transition Temperature | 80.0 | °C | DSC |
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 |
| CLTE - Flow (-30 to 40°C) | 5.1E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | DSC | ||
| 60°C | 1300 | J/kg/°C | |
| 100°C | 1760 | J/kg/°C | |
| 150°C | 1880 | J/kg/°C | |
| 200°C | 1970 | J/kg/°C | |
| 250°C | 2050 | J/kg/°C | |
| Thermal Conductivity (23°C) | 0.21 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 10(23°C) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 23°C, 1 kHz | 2.60 | ||
| 23°C, 1 MHz | 2.40 | ||
| Dissipation Factor | ASTM D150 | ||
| 23°C, 1 kHz | 5.0E-3 | ||
| 23°C, 1 MHz | 0.020 | ||
| Arc Resistance | 158 | sec | ASTM D495 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 108 | ASTM D2457 | |
| Transmittance | ASTM D1003 | ||
| Total | 91.0 | % | |
| Regular | 89.0 | % | |
| Clarity | 85.0 | ASTM D1746 | |
| Haze | 0.80 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 15.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | EMN-A-AC-GV-1 |
| 2 . | 50% RH |
| 3 . | 254 mm/min, Split Tear Method |
| 4 . | 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
| 5 . | 200 mm/min |
| 6 . | 4 mm |
| 7 . | 4 mm |
| 8 . | 4 mm |
| 9 . | 4 mm |
| 10 . | 500 V/sec, Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech T706 | Shanghai Suptech Engineering Plastics Co. Ltd. | PBT | Sup-tech |
| TAROLOX 200 G6 | Taro Plast S.p.A. | PBT+ASA | TAROLOX |
| WACKER® MASTERBATCH AC | Wacker Chemie AG | Silicone | WACKER® |
| NILENE® P15 K20C | Taro Plast S.p.A. | PP Homopolymer | NILENE® |
| EPIGUM EXP/5065 | Crosspolimeri S.p.A. | TPE | EPIGUM |