Latigloss 66 H2 G/50 F2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latigloss |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ygliGG_Latigloss66H2G50F2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product with high mechanical properties and exceptional surface finish based on Polyamide 66 (PA66). Heat stabilised. Glass fibres. Potentially suitable for food/medical contact application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | |||
| Transverse flow : 2.00mm | 0.65 - 0.90 | -- | % | ISO 294-4 |
| Flow : 2.00mm | 0.30 - 0.60 | -- | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.27 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | |||
| -- | -- | 10000 | MPa | ISO 527-2/1 |
| 23°C | 16000 | -- | MPa | ISO 527-2/1 |
| 60°C | 12000 | -- | MPa | ISO 527-2/1 |
| 90°C | 7000 | -- | MPa | ISO 527-2/1 |
| 120°C | 5000 | -- | MPa | ISO 527-2/1 |
| 150°C | 4000 | -- | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | |||
| Fracture | -- | 145 | MPa | ISO 527-2/5 |
| Fracture, 23°C | 230 | -- | MPa | ISO 527-2/5 |
| Fracture, 60°C | 175 | -- | MPa | ISO 527-2/5 |
| Fracture, 90°C | 125 | -- | MPa | ISO 527-2/5 |
| Fracture, 120°C | 95.0 | -- | MPa | ISO 527-2/5 |
| Fracture, 150°C | 70.0 | -- | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | |||
| Fracture | -- | 3.5 | % | ISO 527-2/5 |
| Fracture, 23°C | 2.8 | -- | % | ISO 527-2/5 |
| Fracture, 60°C | 3.2 | -- | % | ISO 527-2/5 |
| Fracture, 90°C | 6.7 | -- | % | ISO 527-2/5 |
| Fracture, 120°C | 7.5 | -- | % | ISO 527-2/5 |
| Fracture, 150°C | 8.0 | -- | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 85 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 235 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 130 | -- | °C | |
| Vicat Softening Temperature | 250 | -- | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 7.0E-6 | -- | cm/cm/°C | ISO 11359-2 |
| Additional Information | Dry | Conditioned | ||
|---|---|---|---|---|
| Dimensional Stability | 66.0 | -- |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech P260 | Shanghai Suptech Engineering Plastics Co. Ltd. | PP, Unspecified | Sup-tech |
| TEREZ PA 6.6 7500 GF30 FL HF /2 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Ferro PP TPP20AF70UL | Ferro Corporation | PP Homopolymer | Ferro PP |
| Kpren 135A | Shandong Xuye New Materials Co., Ltd. | CPE | Kpren |
| OMIKRON LL 150 NAT | TECNOPOL | PP Copolymer | OMIKRON |