LNP™ VERTON™ RV00AE compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yggAIl_LNPVERTONRV00AEcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON RV00AE is a compound based on PA 66 rsin containing Long Glass Fiber. Added features include; Easy Molding. Also known as: LNP* VERTON* Compound RF-700-10 EM Product reorder name: RV00AE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 24 hours | 0.22 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.15 - 0.35 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 265 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 15600 | MPa | ISO 178 |
| Flexural Stress | 370 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2 | ISO 180/1A | ||
| -40°C | 38 | kJ/m² | ISO 180/1A |
| 23°C | 45 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 89 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 152 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 258 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 253 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 6.7E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 288 - 299 | °C | |
| Processing (Melt) Temp | 288 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9735C | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Resalloy™ 165 | Resirene, S.A. de C.V. | Styrene Epoxy Copolymer | Resalloy™ |
| ABSCOM® S130GHR | Polymer Compounders Limited | ABS | ABSCOM® |
| ESTAPROP KUR 0640 TG | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| Piolen® P B50A19 | PiO Kunststoffe GmbH & Co KG | PP Homopolymer | Piolen® P |