LNP™ LUBRICOMP™ DEL36P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ygauaR_LNP-LUBRICOMP-DEL36P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DEL36P is a compound based on Polycarbonate resin containing 30% Carbon Fiber, 15% PTFE. Added features include: Internally Lubricated, Exceptional Processing. Also known as: LNP* LUBRICOMP* Compound DCL-4036 EP Product reorder name: DEL36P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 22100 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 148 | MPa | |
| Break | 148 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 1.3 | % | |
| Break | 1.5 | % | |
| Flexural Modulus 1 | 15400 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 179 | MPa | |
| -- 4 | 177 | MPa | |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.55 | ASTM D3702 Modified | |
| Flexural Strain at Break 5 | 1.5 | % | ISO 178 |
| Wear Factor - Washer | 9.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 6(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 136 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 130 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.6E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 2 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® 1344 FC | A. Schulman Europe | ABS | RONFALIN® |
| Vydyne® R550H NT662 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Multi-Flex® TPE A8502 LC UV | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| NYLOPAK™ 570P | The Dow Chemical Company | Nylon, Unspecified | NYLOPAK™ |
| Diakon® ST45G6 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |