Polifil® Nylon 89MRGFHS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | The Plastics Group |
| Trademark: | Polifil® Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ygae0u_Polifil-Nylon-89MRGFHS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polifil® GFN/MRN 6 reinforced series of compounds provide good heat and dimensional stability. These have been found useful in industrial clamp components as well as bearings. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.90 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6890 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 117 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 2.0 | % | |
| Break, 23°C | 3.0 | % | |
| Flexural Modulus - Tangent (23°C) | 6550 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 96 | J/m | ASTM D256 |
| Gardner Impact (23°C, 12.7 mm) | 0.678 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 216 | °C | |
| 1.8 MPa, Unannealed | 199 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 249 | °C | |
| Middle Temperature | 271 | °C | |
| Front Temperature | 282 | °C | |
| Nozzle Temperature | 282 | °C | |
| Processing (Melt) Temp | 277 to 293 | °C | |
| Mold Temperature | 37.8 to 93.3 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 to 0.517 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reon 60GER01 | Reliance Industries Limited | PVC Homopolymer | Reon |
| RheTech Polypropylene T10P250-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Exxtral™ Performance Polyolefin HMU234 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Elastron® V V601.A85.N | Elastron USA, Inc. | TPV | Elastron® V |
| OTECH PVC OW135 - Riser Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |