Celanex® 6400-2
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ygaEwf_Celanex-6400-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% glass/mineral reinforced polyester, providing warp resistance and improved surface finish. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.66 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 11000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.8 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 235 - 255 | °C | |
| Front Temperature | 235 - 255 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65.0 - 93.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 250°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 52G1 V25 GREY R7035 CF | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| VITAMIDE® AI10BK6201/2C | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Desmopan® 795 U | Covestro - PUR | TPU, Unspecified | Desmopan® |
| Sylvin 5225-92 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ Lexan_WR5210R compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |