XANTAR® LDS 3710
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | XANTAR® LDS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ygRdYi_XANTAR-LDS-3710.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Laser Direct Structuring (LDS)*, Vicat 120°C, Black color only *The compound is intended specifically for the use in the process of manufacturing conducting path designs according to the German application of the patent 101 32 092 of LPKF Laser & Electronics AG. Please address straight to LPKF Laser & Electronics AG (www.LPKF.de). |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2250 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 60 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C | 40 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | |||
| -20°C 1 | 4.00 | J | Internal Method |
| 23°C | 35.0 | J | ISO 6603-2 |
| 23°C 2 | 10.0 | J | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 102 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 122 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 7.0E-5 | cm/cm/°C | |
| Transverse | 7.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity (1.00 GHz) | 2.80 | IEC 60250 | |
| Dissipation Factor (1.00 GHz) | 5.0E-3 | IEC 60250 |
| Note Message | |
|---|---|
| 1 . | Part with rib, Based on ISO 6603-2 |
| 2 . | Part with rib, Based on ISO 6603-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4002 A FR | RTP Company | PPA | RTP |
| SKYBOND® 701 | Industrial Summit Technology Co. | API | SKYBOND® |
| Starflam RF0077P | Eurostar Engineering Plastics | Nylon 66/6 | Starflam |
| Epoxies, Ect. 50-3100 (Cat. 150) | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Sumiliteresin® PR-51541B | SBHPP | Phenolic | Sumiliteresin® |