Infino XP-2165MC
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ygEmpp_Infino-XP-2165MC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino XP-2165MC is a Polyphenylene Sulfide (PPS) product filled with glass\mineral. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.96 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (315°C/5.0 kg) | 80 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.25 to 0.80 | % | ASTM D955, ISO 2577 |
| Water Absorption | |||
| 23°C, 24 hr | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 15000 | MPa | ASTM D638 |
| -- | 10700 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 150 | MPa | ASTM D638 |
| Yield | 150 | MPa | ISO 527-2/50 |
| Break 3 | 160 | MPa | ASTM D638 |
| Break | 188 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 1.5 | % | ASTM D638 |
| Break | 3.2 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 18000 | MPa | ASTM D790 |
| -- 6 | 18000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 200 | MPa | ASTM D790 |
| -- 8 | 240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 59 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 53 | J/m | ASTM D256 |
| 23°C 9 | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 284 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 285 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 283 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 270 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 272 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 274 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 10(23°C) | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Constant (10 MHz) | 5.00 | ASTM D150 | |
| Dissipation Factor (10 MHz) | 7.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 280 to 290 | °C | |
| Middle Temperature | 290 to 300 | °C | |
| Front Temperature | 310 to 320 | °C | |
| Nozzle Temperature | 330 | °C | |
| Mold Temperature | 120 to 150 | °C | |
| Injection Pressure | 49.0 to 127 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ 205 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| SLOVALEN® PH 92 T 30 | Plastcom | PP, Unspecified | SLOVALEN® |
| Nylene® 733 | Custom Resins Group | Nylon 6 | Nylene® |
| Polybilt™ Bitumen Modifier 101 | ExxonMobil Chemical | LDPE | Polybilt™ Bitumen Modifier |
| Hifax CA 1110 G4 LS 1740 | LyondellBasell Industries | PP Copolymer | Hifax |