VECTOR® 4114N

Category:	SIS+SI , Styrene Isoprene Styrene + SI Block Copolymer
Manufacturer:	TSRC Corporation
Trademark:	VECTOR®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	yfRUZ9_VECTOR-4114N.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Blend of linear SIS triblock and SI diblock copolymer. Contains ~42% SI diblock copolymer. Low styrene, very low modulus. VECTOR 4114A and VECTOR 4114N styrenic block copolymers are blended products composed of a linear SIS triblock copolymer and an SI diblock copolymer. They are softer than VECTOR 4113A SIS/SI due to higher diblock content, making them well-suited for use in hot melt pressure sensitive adhesives, elastomer compounds and photopolymer plate applications. VECTOR 4114A SIS/SI is offered as a dense pellet supplied from the United States. VECTOR 4114N SIS/SI is offered as a porous pellet supplied from China.

Message

Blend of linear SIS triblock and SI diblock copolymer.

Contains ~42% SI diblock copolymer.

Low styrene, very low modulus.

VECTOR 4114A and VECTOR 4114N styrenic block copolymers are blended products composed of a linear SIS triblock copolymer and an SI diblock copolymer. They are softer than VECTOR 4113A SIS/SI due to higher diblock content, making them well-suited for use in hot melt pressure sensitive adhesives, elastomer compounds and photopolymer plate applications.

VECTOR 4114A SIS/SI is offered as a dense pellet supplied from the United States.

VECTOR 4114N SIS/SI is offered as a porous pellet supplied from China.

General Information
Features	Soft
Uses	Adhesives
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.918	g/cm³	ASTM D792
Apparent Density	0.33	g/cm³	ASTM D1895
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	25	g/10 min	ASTM D1238
Bound Styrene	15.0	%
Ash Content	0.6	wt%
Solution Viscosity - in 25 wt% Toluene (25°C)	700	mPa·s

Additional Information	Nominal Value	Unit
Diblock Content	42.0	wt%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 1 sec, Compression Molded)	26		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(300% Strain)	0.700	MPa	Internal Method
Tensile Strength ²(Break)	13.0	MPa	Internal Method
Tensile Elongation ³(Break)	1500	%	Internal Method

Note Message
1 .	Compression Molded
2 .	Compression Molded
3 .	Compression Molded

Resin Grade	Manufacturer	Category	Trademark
POLYSTONE® D black nuclear	Röchling Engineering Plastics SE & Co. KG	HMWPE	POLYSTONE®
RTP 800 AR 15 TFE 20	RTP Company	Acetal (POM) Copolymer	RTP
Sup-tech T703	Shanghai Suptech Engineering Plastics Co. Ltd.	PBT	Sup-tech
VESTOLIT® E 7004	VESTOLIT GmbH & Co. KG	PVC, Unspecified	VESTOLIT®
NEXT REGRIND PC 500-300RG	NEXT Specialty Resins, Inc.	PC	NEXT REGRIND