Lucel® FW700S
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yeygCZ_Lucel-FW700S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucel®FW700S is a polyoxymethylene (POM) copolymer material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Lucel®The main features of FW700S are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 2.0 - 2.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 53.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 70 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 78.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, annealed, 6.40mm | 155 | °C | ASTM D648 |
| 1.8 MPa, annealed, 6.40mm | 105 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.950 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 110 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 160 - 180 | °C | |
| Middle Temperature | 170 - 190 | °C | |
| Front Temperature | 180 - 200 | °C | |
| Nozzle Temperature | 180 - 200 | °C | |
| Processing (Melt) Temp | 200 - 220 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Back Pressure | 0.490 - 3.04 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.1% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNISOFT ADHESION™ AD-80A-NT-1-35 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT ADHESION™ |
| Hanwha Total PE 530G | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LDPE | Hanwha Total PE |
| Kazan HDPE PEBO-285D | Kazanorgsintez Joint Stock Company | HDPE | Kazan HDPE |
| LG PMMA HI835H | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| Sumikon® FM-TC122 | SBHPP | PC | Sumikon® |