Ducor® 2600 TC
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Ducor Petrochemicals BV |
| Trademark: | Ducor® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yenFd7_Ducor-2600-TC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ducor 2600TC is a hetrophasic block copolymer. It shows a very high fluidity and good impact resistance. Typical applications are thinwalled packaging, housewares. Food Contact Applications: This grade is in compliance with most regulations regarding food contact applications (EU, FDA). Specific information is available upon request. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 48 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/30) | 44.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 950 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 19.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.0 | % | |
| Break | > 50 | % | |
| Shear Modulus | 500 | MPa | ISO 6721-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| -20°C | 4.5 | kJ/m² | |
| 0°C | 9.0 | kJ/m² | |
| 23°C, Partial Break | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 130 | kJ/m² | |
| -20°C | 150 | kJ/m² | |
| 0°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 4.5 | kJ/m² | |
| -20°C | 5.5 | kJ/m² | |
| 0°C | 9.0 | kJ/m² | |
| 23°C, Partial Break | 18 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 78.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 48.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 142 | °C | ISO 306/A |
| -- | 56.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 163 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA210SG30 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Stanyl® TW200F3 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Vyncolit® RX®1366FR | Vyncolit N.V. | DAP | Vyncolit® |
| Carbotex KG-20MRA | Kotec Corporation | PC | Carbotex |
| LNP™ LUBRICOMP™ PFL38S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |