MALECCA K-090
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | MALECCA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yeM8I1_MALECCA-K-090.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MALECCA K-090 is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| 23°C | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 114 | ASTM D785 | |
| R-Scale | 113 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 43.0 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 49.0 | MPa | |
| Break | 38.0 | MPa | |
| Nominal Tensile Strain at Break | 30 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2450 | MPa | ASTM D790 |
| -- 3 | 2550 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 72.0 | MPa | ASTM D790 |
| -- 5 | 74.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 22 | kJ/m² | ISO 179 |
| Notched Izod Impact | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed 6 | 97.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 87.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 107 | °C | ISO 306/B, ASTM D1525 7 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 210 to 240 | °C | |
| Front Temperature | 220 to 250 | °C | |
| Nozzle Temperature | 220 to 245 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.490 to 0.981 | MPa | |
| Screw Speed | 50 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 15 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 15 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Edgewise |
| 7 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pristene RM5100 | PolyMirae | Polyolefin, Unspecified | Pristene |
| Chemlon® 109-14 GH | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| EVICOM™ EX2/235 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| Generic PPE+PS - Unspecified | Generic | PPE+PS | Generic |
| LEXAN™ EXL1890T resin | SABIC Innovative Plastics | PC | LEXAN™ |