Next ABS SXF-01BK
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ycsRk9_Next-ABS-SXF-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description ABS Un Filled FR Black Compound Product Applications It is an ideal for an structrual application such as Transformer housing,switches,sheving & air conditioner components. Benefits Good Toughned &chemical resistance ,Excellent moldability, UL94- V0 /5VA Rated . |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | |
| Across Flow | 0.40 | % | |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.32 | % | |
| Saturation 1 | 0.75 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2340 | MPa | ASTM D638 |
| Tensile Strength | 41.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 2700 | MPa | ASTM D790 |
| Flexural Strength | 75.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 105 | °C | |
| 1.8 MPa, Unannealed | 95.0 | °C | |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Arc Resistance | 30.0 | sec | ASTM D495 |
| Arc Resistance | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | > 400 | V | UL 746 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | 22 | sec | UL 746 |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 70.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 210 to 215 | °C | |
| Middle Temperature | 215 to 220 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Mold Temperature | 45.0 to 65.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VECTRA® A515 | Celanese Corporation | LCP | VECTRA® |
| 3M™ Dyneon™ PTFE Compound TF 7149 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| Ferro PP LPP40BC85UL-WH | Ferro Corporation | PP, Unspecified | Ferro PP |
| Lucent PC PC/PBT-1550 | Lucent Polymers, Inc. | PC+PBT | Lucent PC |
| Optix® CA-82 FDA | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |