THERMOLAST® V TV6VAZ (Series: LTP/PA)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | KRAIBURG TPE |
| Trademark: | THERMOLAST® V |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ycW4pp_THERMOLASTVTV6VAZSeriesLTPPA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The LTP/PA Series is your material solution for sealings requiring high temperature resistance.The compounds are characterized by an excellent adhesion to PA. Typical applications
Material advantages
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 60 | ISO 7619 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(Break) | 6.00 | MPa | ISO 37 |
| Tensile Elongation 2(Break) | 450 | % | ISO 37 |
| Tear Strength 3 | 15 | kN/m | ISO 34-1 |
| Compression Set 4 | ISO 815 | ||
| 23°C, 72 hr | 20 | % | ISO 815 |
| 70°C, 24 hr | 35 | % | ISO 815 |
| 120°C, 24 hr | 60 | % | ISO 815 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Adhesion to PA6 - (D) | 7.0 | kN/m | VDI 2019 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60 - 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 230 - 245 | °C | |
| Middle Temperature | 250 - 260 | °C | |
| Front Temperature | 260 - 270 | °C | |
| Mold Temperature | 40 - 60 | °C | |
| Injection Pressure | 2.00 - 100 | MPa | |
| Back Pressure | 2.00 - 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Type S2, 200 mm/min |
| 2 . | Type S2, 200 mm/min |
| 3 . | Method B, right-angle specimen (cut) |
| 4 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® MJ6301C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| TECHNYL STAR™ SX 218L2 V60 BLACK JA6A | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR™ |
| SPESIN® KP213G15SI | Kolon Plastics, Inc. | PBT | SPESIN® |
| TEREZ ABS 1081 | TER HELL PLASTIC GMBH | ABS | TEREZ ABS |
| Texalan® 4 Series 498A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 4 Series |