Durethan® BKV 315 Z H2.0 901510

Category:	Nylon 6 , Polyamide 6
Manufacturer:	LANXESS Asia/Pacific
Trademark:	Durethan®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ycGsbt_DurethanBKV315ZH20901510.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PA 6, 15 % glass fibers, blow molding, improved impact strength, heat-aging stabilized

General Information
Filler / Reinforcement	Glass fiber reinforced material, 15% filler by weight
Additive	heat stabilizer
Features	Impact resistance, good Thermal Stability
Processing Method	Blow molding

Physical	Dry	Conditioned	Unit	Test Method
Density (23°C)	1.20	--	g/cm³	ISO 1183
Apparent Density	0.70	--	g/cm³	ISO 60
Molding Shrinkage				ISO 2577
Vertical flow direction : 280°C, 2.00mm ¹	0.60	--	%	ISO 2577
Vertical flow direction : 120°C, 4 hours, 2.00mm ²	0.10	--	%	ISO 2577
Flow direction : 280°C, 2.00mm ³	0.90	--	%	ISO 2577
Flow direction : 120°C, 4 hours, 2.00mm ⁴	0.20	--	%	ISO 2577

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	140	--	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	5300	2500	MPa	ISO 527-2/1
Tensile Stress (Break, 23°C)	105	55.0	MPa	ISO 527-2/5
Tensile Strain (Break, 23°C)	5.0	19	%	ISO 527-2/5
Flexural Modulus ⁵(23°C)	4800	2300	MPa	ISO 178/A
Flexural Stress				ISO 178/A
3.5% strain, 23°C	150	55.0	MPa	ISO 178/A
23°C ⁶	165	75.0	MPa	ISO 178/A
Flexural Strain at Flexural Strength ⁷(23°C)	5.5	7.5	%	ISO 178/A

Flammability	Dry	Conditioned	Unit	Test Method
Burning Behavior ⁸	passed	--		ISO 3795

Additional Information	Dry	Conditioned		Test Method
ISO Shortname	PA 6-HI, BHR, 14-050, GF15	--		ISO 1874

Injection	Dry	Unit	Test Method
Residual Moisture Content	0.0 - 0.060	%	Karl Fisher

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	< 10	10	kJ/m²	ISO 179/1eA
23°C	15	30	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	85	90	kJ/m²	ISO 179/1eU
23°C	80	110	kJ/m²	ISO 179/1eU
Notched Izod Impact				ISO 180/1A
-30°C	10	< 10	kJ/m²	ISO 180/1A
23°C	15	30	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength				ISO 180/1U
-30°C	70	65	kJ/m²	ISO 180/1U
23°C	65	95	kJ/m²	ISO 180/1U
Multi-Axial Instrumented Impact Energy				ISO 6603-2
-30°C	2.50	--	J	ISO 6603-2
23°C	4.90	--	J	ISO 6603-2
Multi-Axial Instrumented Impact Peak Force				ISO 6603-2
-30°C	630	--	N	ISO 6603-2
23°C	1200	--	N	ISO 6603-2

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	210	--	°C	ISO 75-2/B
1.8 MPa, not annealed	175	--	°C	ISO 75-2/A
8.0 MPa, not annealed	58.0	--	°C	ISO 75-2/C
Melting Temperature ⁹	221	--	°C	ISO 11357-3
Linear thermal expansion coefficient				ISO 11359-2
Flow : 23 to 55°C	4.0E-5	--	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	1.3E-4	--	cm/cm/°C	ISO 11359-2

Electrical	Dry	Conditioned	Unit	Test Method
Comparative Tracking Index (Solution A)	375	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
1.60 mm	HB	--		UL 94
3.20 mm	HB	--		UL 94

Injection	Dry	Unit	Test Method
Drying Temperature - Dry Air Dryer	80.0	°C
Drying Time - Dry Air Dryer	2.0 - 6.0	hr
Processing (Melt) Temp	270 - 290	°C
Mold Temperature	80.0 - 120	°C

Note Message
1 .	60x60x2mm, 80°C MT, 600 bar
2 .	60x60x2mm
3 .	60x60x2mm, 80°C MT, 600 bar
4 .	60x60x2mm
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	2 mm/min
8 .	US-FMVSS302
9 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
TYNEP® E4450	Tyne Plastics LLC.	PET	TYNEP®
ALFATER XL® A50I 4FC0000	ALBIS PLASTIC GmbH	TPV	ALFATER XL®
Geon™ Vinyl Flexible XV3830B	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible
Karina WHITE PVC COMPOUND -E 839-10/ 19-Y-CR	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LNP™ LUBRICOMP™ WFL369 compound	SABIC Innovative Plastics	PBT	LNP™ LUBRICOMP™