Terluran® HI-10

Category:	ABS , Acrylonitrile Butadiene Styrene
Manufacturer:	INEOS Styrolution Group GmbH
Trademark:	Terluran®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ybb26p_Terluran-HI-10.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
Terluran HI-10 is an medium flow, injection molding grade with very high resistance to impact with excellent heat distortion and suitable for injection molding and extrusion.

General Information
Features	Low Temperature Impact Resistance Medium Flow Medium Rigidity Ultra High Impact Resistance Ultra High Toughness
Uses	Appliances Compounding Housings Lawn and Garden Equipment
Forms	Pellets
Processing Method	Compounding Extrusion Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.03	g/cm³	ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR)			ASTM D1238
200°C/5.0 kg	0.10	g/10 min
220°C/10.0 kg	8.0	g/10 min
Melt Volume-Flow Rate (MVR)
230°C/3.8 kg	1.70	cm³/10min	ASTM D1238
220°C/10.0 kg	5.50	cm³/10min	ISO 1133
Molding Shrinkage
Flow	0.40 to 0.70	%	ASTM D955
--	0.40 to 0.70	%	ISO 294-4
Water Absorption
Saturation, 23°C	1.0	%	ASTM D570, ISO 62
Equilibrium, 23°C, 50% RH	0.21	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	95		ASTM D785
Ball Indentation Hardness	74.0	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
--	2000	MPa	ASTM D638
--	1900	MPa	ISO 527-2
Tensile Strength
Yield, 23°C	43.0	MPa	ASTM D638
Yield, 23°C	38.0	MPa	ISO 527-2
Tensile Strain
Yield, 23°C	2.8	%	ISO 527-2
Break	3.5	%	ASTM D638
Nominal Tensile Strain at Break (23°C)	9.0	%	ISO 527-2
Flexural Modulus	2050	MPa	ASTM D790
Flexural Strength
--	66.0	MPa	ASTM D790
--	56.0	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179
-30°C	13	kJ/m²
23°C	35	kJ/m²
Charpy Unnotched Impact Strength			ISO 179
-30°C	140	kJ/m²
23°C	No Break
Notched Izod Impact
-30°C	120	J/m	ASTM D256
-18°C	180	J/m	ASTM D256
23°C	450	J/m	ASTM D256
-30°C	14	kJ/m²	ISO 180/A
23°C	36	kJ/m²	ISO 180/A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed	93.9	°C	ASTM D648
0.45 MPa, Annealed	102	°C	ASTM D648
0.45 MPa, Annealed	97.0	°C	ISO 75-2/B
1.8 MPa, Unannealed	85.6	°C	ASTM D648
1.8 MPa, Annealed	97.8	°C	ASTM D648
1.8 MPa, Annealed	93.0	°C	ISO 75-2/A
Vicat Softening Temperature
--	103	°C	ISO 306/A50
--	90.0	°C	ISO 306/B50
CLTE - Flow	8.0E-5 to 1.1E-4	cm/cm/°C	ISO 11359-2
Thermal Conductivity	0.17	W/m/K	DIN 52612

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity
--	> 1.0E+15	ohms·cm	ASTM D257
--	1.0E+15	ohms·cm	IEC 60093
Dielectric Constant
1.00 mm, 1 MHz	2.80		ASTM D150
100 Hz	2.90		IEC 60250
1 MHz	2.80		IEC 60250
Dissipation Factor			IEC 60250
100 Hz	5.4E-3
1 MHz	8.2E-3

Optical	Nominal Value	Unit	Test Method
Yellowness Index	15	YI	DIN 6167

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	2.0 to 4.0	hr
Processing (Melt) Temp	230 to 260	°C
Mold Temperature	30.0 to 60.0	°C
Injection Velocity	200	mm/sec

Resin Grade	Manufacturer	Category	Trademark
CALIBRE™ 301EP-37	Trinseo	PC	CALIBRE™
Arnite® T06 200	DSM Engineering Plastics	PBT	Arnite®
Hypro® PP-CP 10/10	Entec Polymers	PP Impact Copolymer	Hypro®
LEXAN™ LUX7630C resin	SABIC Innovative Plastics	PC	LEXAN™
Plenco 03356 (Compression)	Plastics Engineering Co.	Phenolic	Plenco