Sarlink® TPV X4765B42
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ybEtkI_Sarlink-TPV-X4765B42.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SARLINK® 4000 series are engineered materials designed primarily for demanding automotive applications. SARLINK® X4765B-42 exhibits excellent compression set and weatherability. The material is developed especially for injection moulded applications featuring high flow and UV-stability. Applications include window encapsulation, spoiler extensions and other intricate and high flow demanding applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.908 | g/cm³ | ASTM D792 |
| -- | 0.910 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ASTM D2240, ISO 868 | ||
| Shore A, 5 sec, Extruded | 62 | ||
| Shore A, 5 sec, Injection Molded | 65 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| Across Flow : 100% Strain | 2.30 | MPa | |
| Flow : 100% Strain | 2.90 | MPa | |
| Tensile Stress | ASTM D412, ISO 37 | ||
| Across Flow : Break | 5.10 | MPa | |
| Flow : Break | 4.90 | MPa | |
| Tensile Elongation | ASTM D412, ISO 37 | ||
| Across Flow : Break | 400 | % | |
| Flow : Break | 340 | % | |
| Tear Strength - Across Flow | |||
| -- | 25 | kN/m | ASTM D624 |
| -- 1 | 25 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 22 hr | 23 | % | |
| 70°C, 22 hr | 32 | % | |
| 125°C, 70 hr | 48 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | ASTM D573, ISO 188 | ||
| 135°C, 1000 hr | -18 | % | |
| 100% Strain 135°C, 1000 hr | 1.0 | % | |
| 150°C, 168 hr | -20 | % | |
| 100% Strain 150°C, 168 hr | 0.0 | % | |
| Change in Tensile Strain at Break in Air - Across Flow | ASTM D573, ISO 188 | ||
| 135°C, 1000 hr | -22 | % | |
| 150°C, 168 hr | -24 | % | |
| Change in Shore Hardness in Air | ASTM D573, ISO 188 | ||
| Shore A, 135°C, 1000 hr | 1.0 | ||
| Shore A, 150°C, 168 hr | 1.0 | ||
| Change in Volume (135°C, 70 hr, in IRM 903 Oil) | 84 | % | ISO 1817, ASTM D471 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary, @ 206/s | |||
| 200°C | 210 | Pa·s | ASTM D3835 |
| 200°C | 210 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 205 | °C | |
| Middle Temperature | 180 to 205 | °C | |
| Front Temperature | 180 to 205 | °C | |
| Nozzle Temperature | 185 to 210 | °C | |
| Processing (Melt) Temp | 185 to 210 | °C | |
| Mold Temperature | 10.0 to 55.0 | °C | |
| Back Pressure | 0.100 to 1.00 | MPa | |
| Screw Speed | 100 to 200 | rpm |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8215-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| DI-COAT R-4721LV/7 | Hapco Inc. | TP, Unspecified | DI-COAT |
| Fainplast PVC KL 90 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| GAPEX® RPP20EU65GY | Ferro Corporation | PP, Unspecified | GAPEX® |
| LUVOCOM® 1/SCF/30 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |