TOTAL Polypropylene PPH 3281
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yb6DHt_TOTAL-Polypropylene-PPH-3281.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The high melt strength of TOTAL Polypropylene 3281 allows uniform draw down during processing, resulting in maximum line speeds and a good balance of physical properties. Excellent polymer stability of TOTAL Polypropylene 3281 produces consistent product properties during extrusion, even with the use of regrind. TOTAL Polypropylene 3281 complies with all applicable FDA regulations and may be used under these provisions for food contact applications. TOTAL Polypropylene 3281 is recommended for sheet and strapping applications where high melt strength and high extrusion speeds are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.3 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 | |
| Durometer Hardness (Shore D) | 81 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1520 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 33.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 1380 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256A |
| Unnotched Izod Impact (23°C) | 1600 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Melting Temperature | 166 | °C | DSC |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 199 to 232 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 8101 | Premix, Inc. | Polyester, TP | Premi-Glas® |
| Unipren® Elastomers A3 CRLA010 65D EG06S1 UP344 | Petropol Industry and Trade of Polymers LTDA | SBC | Unipren® Elastomers |
| Exelene® HDPE 7000 | Montachem International, Inc. | HDPE, HMW | Exelene® HDPE |
| ENVIRON® ENV39-NC440 | ENVIROPLAS®, Inc. | PC+PBT | ENVIRON® |
| Panlite® B-4110R | TEIJIN LIMITED | PC | Panlite® |