Karina CLEAR PVC COMPOUND -E 70850/200-IS
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yavPeM_Karina-CLEAR-PVC-COMPOUND--E-70850-200-IS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Karina CLEAR PVC COMPOUND -E 70850/200-IS is a Polyvinyl Chloride product. It is available in Latin America. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.23 to 1.29 | g/cm³ | ASTM D792 |
| Cadmium Content | < 50 | ppm | IEC 62321 |
| Chromium Content | < 100 | ppm | IEC 62321 |
| Color | OK | ME 12 | |
| Mercury Content | < 100 | ppm | IEC 62321 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Lead Content | < 100 | ppm | IEC 62321 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 83 to 87 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 14.7 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 200 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 14.7 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 200 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.5E+14 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REXtac® APAO RT 2280 | Huntsman Corporation | PAO | REXtac® APAO |
| SCHULASINT™ F5400 | ICO Polymers EMEA, A Division of A. Schulman | PP Random Copolymer | SCHULASINT™ |
| TECOLITE KM-350(G) | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| Greenflex® ML 50 F | Versalis S.p.A. | EVA | Greenflex® |
| LUVOCOM® GS-58 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |