NORYL™ PX4605 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yaG79v_NORYL-PX4605-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPE+PS blend. 20% Glass reinforced. High heat. Dimensional stability. Suitable for automotive and E/E applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.21 | g/cm³ | ASTM D792 |
| -- | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | Internal Method |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 7560 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 112 | MPa | |
| Break 2 | 110 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 2.4 | % | |
| Break 3 | 2.4 | % | |
| Flexural Modulus | ASTM D790 | ||
| 50.0 mm Span 4 | 5520 | MPa | |
| 100 mm Span 5 | 5240 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Yield, 100 mm Span 6 | 148 | MPa | |
| Break, 50.0 mm Span 7 | 170 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 100 | J/m | |
| 23°C | 110 | J/m | |
| Instrumented Dart Impact (23°C, Total Energy) | 20.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 160 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 154 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 154 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 266 to 316 | °C | |
| Middle Temperature | 277 to 321 | °C | |
| Front Temperature | 288 to 327 | °C | |
| Nozzle Temperature | 299 to 327 | °C | |
| Processing (Melt) Temp | 299 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | 2.6 mm/min |
| 7 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2740 S-60A | RTP Company | SEBS | RTP |
| Ultramid® A3ZG6 | BASF Corporation | Nylon 66 | Ultramid® |
| AKROLOY® PA GF 60 black (2844) | AKRO-PLASTIC GmbH | Nylon 66+Nylon 6I/6T | AKROLOY® |
| PCC HD 5502 GA | PCC Plastics & Consultations Center | HDPE | PCC |
| ALCOM® PA66 910/1.3 CF/GF30 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |