Order Products : sales@su-jiao.com
SABIC® FORTIFY™ C3080
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® FORTIFY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yYqVla_SABICFORTIFYC3080.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® FORTIFY™ C3080 is an ethylene octene copolymer produced by solution polymerization using metallocene catalyst. This product is available as free flowing pellets. SABIC® FORTIFY™ C3080 is designed as a high performance copolymer modifier to provide superior toughness, softness and optical properties. It provides excellent flow properties too. Typical applications are impact modifier in thermoplastic olefin compounds, footwear midsoles and wire and cable extrusion. Please take notice of specific storage and handling conditions. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.880 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 11 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 1 sec | 78 | ASTM D2240 | |
| Shaw D, 1 sec | 24 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant | 3.30 | MPa | ASTM D638 |
| Tensile Strength (Break) | 11.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 900 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 19.6 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 1 | 41.2 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -49.0 | °C | Internal method |
| Melting Temperature | 68.0 | °C | Internal method |
| Additional Information |
|---|
| All physical properties were measured on compression molded specimens. |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravamid® B MF20 | Ravago Group | Nylon 6 | Ravamid® |
| RANPELEN SB-740D | Lotte Chemical Corporation | PP Random Copolymer | RANPELEN |
| Shandong PA/PP PA6/PP | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 6+PP | Shandong PA/PP |
| TOTAL Polypropylene Lumicene® M 6823 MZ | TOTAL Refining & Chemicals | PP Copolymer | TOTAL Polypropylene |
| Adell PP ER-34 | Adell Plastics, Inc. | PP Homopolymer | Adell PP |