Clariant PC PC-020-L
| Category: | PC , Polycarbonate |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yYQtwx_Clariant-PC-PC-020-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clariant PC PC-020-L is a Polycarbonate (PC) material filled with 20% glass fiber. It is available in North America for injection molding. Important attributes of Clariant PC PC-020-L are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 5170 | MPa | ASTM D790 |
| Flexural Strength | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 75 | J/m | ASTM D256 |
| Tensile Impact Strength | 94.6 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 141 | °C | |
| 1.8 MPa, Unannealed | 138 | °C | |
| Melting Temperature | 257 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 288 to 304 | °C | |
| Middle Temperature | 299 to 316 | °C | |
| Front Temperature | 304 to 338 | °C | |
| Nozzle Temperature | 304 to 338 | °C | |
| Processing (Melt) Temp | 288 to 299 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Injection Pressure | 110 to 138 | MPa | |
| Back Pressure | 0.345 to 1.38 | MPa | |
| Screw Speed | 60 to 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 8T | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| SuperLite® SL551800-100 (4.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| WELLAMID Nylon 6000 MRGV 20/10 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| NANCAR® 1051 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| ACCUTECH™ CP0435G43CV | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |