Vydyne® GW350 NT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yV6wpP_Vydyne-GW350-NT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C, 2.00 mm | 1.8 | % | |
| Flow : 23°C, 2.00 mm | 1.3 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 83.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 17 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3340 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.4 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (23°C) | 4.4 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | °C | ISO 75-2/A |
| Melting Temperature | 263 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.00 mm) | 14 | kV/mm | IEC 60243 |
| Arc Resistance (3.00 mm) | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (3.00 mm) | 250 to 399 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 0.400 mm | PLC 0 | ||
| 0.750 mm | PLC 0 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 0 | ||
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.400 mm | PLC 4 | ||
| 0.750 mm | PLC 4 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 0 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-2 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.400 mm | 960 | °C | |
| 0.750 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.400 mm | 930 | °C | |
| 0.750 mm | 900 | °C | |
| 1.50 mm | 850 | °C | |
| 3.00 mm | 825 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 50 | % | |
| Rear Temperature | 260 to 290 | °C | |
| Middle Temperature | 260 to 290 | °C | |
| Front Temperature | 260 to 290 | °C | |
| Nozzle Temperature | 260 to 290 | °C | |
| Processing (Melt) Temp | 270 to 285 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PPX/NY-G10 | Polymer Resources Ltd. | PPE+PS+Nylon | PRL |
| Vydyne® R633 | Ascend Performance Materials Operations LLC | Nylon 66/6 | Vydyne® |
| 3M™ Dyneon™ Fluoroplastic FEP 6301Z | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| Lucky Enpla LKG | Lucky Enpla Co LTD | ABS | Lucky Enpla |
| POCAN® B 3215 XF 000000 | LANXESS Asia/Pacific | PBT | POCAN® |