NANCAR® 1082
| Category: | NBR , Acrylonitrile Butadiene Rubber |
| Manufacturer: | Nantex Industry Co., Ltd. |
| Trademark: | NANCAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yUQYrB_NANCAR-1082.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NANCAR® 1082 is a medium high acrylonitrile rubber included with 50 phr of Di(2-ethylhexyl)phthalate (DEHP). NANCAR® 1082 can be considered as a plasticizer master batch with are used in conjunction with standard NANCAR NBR and other rubbers where the needs demand. It offers outstanding processing characteristics with the advantages of better dispersion, low power consumption and time savings especially for low durometer NBR products. NANCAR® 1082 is recommended for use in soft rollers, high extending and low durometer items. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mooney Viscosity (ML 1+4, 100°C) | 45 | MU | ASTM D1646 |
| Acrylonitrile Content - Bound | 31.5 | % | Internal Method |
| Stabilizer | Non-staining |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 1(Shore A) | 50 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2(300% Strain) | 8.04 | MPa | ASTM D412 |
| Tensile Strength 3(Yield) | 13.7 | MPa | ASTM D412 |
| Tensile Elongation 4(Break) | 500 | % | ASTM D412 |
| Compression Set 5(100°C, 70 hr) | 30 | % | ASTM D395 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 6(100°C, 70 hr) | -5.0 | % | ASTM D865 |
| Change in Ultimate Elongation in Air 7(100°C, 70 hr) | -35 | % | ASTM D865 |
| Change in Durometer Hardness in Air 8(Shore A, 100°C, 70 hr) | 5.0 | ASTM D865 | |
| Change in Tensile Strength 9 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | 14 | % | |
| 100°C, 70 hr, in ASTM #3 Oil | 13 | % | |
| Change in Ultimate Elongation 10 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | -32 | % | |
| 100°C, 70 hr, in ASTM #3 Oil | -22 | % | |
| Change in Durometer Hardness 11 | ASTM D471 | ||
| Shore A, 100°C, 70 hr, in ASTM #1 Oil | 20 | ||
| Shore A, 100°C, 70 hr, in ASTM #3 Oil | 10 | ||
| Change in Volume 12 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM Oil #1 | -22 | % | |
| 100°C, 70 hr, in ASTM Oil #3 | -8.0 | % |
| Note Message | |
|---|---|
| 1 . | Cured for 6.00 min at 160°C |
| 2 . | Cured for 6.00 min at 160°C |
| 3 . | Cured for 6.00 min at 160°C |
| 4 . | Cured for 6.00 min at 160°C |
| 5 . | Cured for 11.0 min at 160°C |
| 6 . | Cured for 6.00 min at 160°C |
| 7 . | Cured for 6.00 min at 160°C |
| 8 . | Cured for 6.00 min at 160°C |
| 9 . | Cured for 6.00 min at 160°C |
| 10 . | Cured for 6.00 min at 160°C |
| 11 . | Cured for 6.00 min at 160°C |
| 12 . | Cured for 6.00 min at 160°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMLLOY PN300G4 | Polyram Ram-On Industries | PPE+PS | RAMLLOY |
| Nypol® PA B3 G35 HS PRTA011 NT391 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Grilon® TSS/4 LF 2 | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| INEOS PP 401-CB50 | INEOS Olefins & Polymers Europe | PP Impact Copolymer | INEOS PP |
| LONGLITE® PBT 4830-BK | CCP Group | PBT | LONGLITE® PBT |