Borealis PP HF700SA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yU3d2P_Borealis-PP-HF700SA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HF700SA is a polypropylene homopolymer intended for injection moulding. This material has excellent balanced mechanical properties and is easy to process. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.50 - 0.60 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 21 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.5 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 70.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 34.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 15 | kJ/m² | ISO 179/1eU |
| 23°C | 80 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 94.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 53.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A50 |
| -- | 90.0 | °C | ISO 306/B50 |
| Ball Indentation Temperature 1 | 125 | °C | IEC 60695-10-2 |
| RTI Elec (2.00 mm) | 120 | °C | UL 746 |
| RTI Imp (2.00 mm) | 120 | °C | UL 746 |
| RTI (2.00 mm) | 120 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 2(2.00 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (20°, 2.00 µm) | 70 | DIN 67530 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Back pressure: Low to mediumScrew speed: Low to mediumFlow front speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | thickness: 2 mm |
| 2 . | thickness: 0.8 to 3 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® D6855 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SABIC® PPcompound G3230AE | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PPcompound |
| SILVER® ABS 350D | Guangdong Silver Age Sci & Tech. Co., Ltd | ABS+PVC | SILVER® |
| Chemical Resources PMMA1100 | Chemical Resources, Inc. | Acrylic (PMMA) | Chemical Resources |
| Formolon® 622R | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |