LNP™ COLORCOMP™ 325C compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yTQ1sG_LNPCOLORCOMP325Ccompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* COLORCOMP* 325C is a general purpose, unreinforced PBT resin. Added features of this grade include improved processing. Good for applications such as sprinklers, nozzles, pumps, door handles, tank covers, pens and pencils. Also known as: LNP* COLORCOMP* Compound 325 Product reorder name: 325C |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Specific Volume | 0.770 | cm³/g | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 1.5 - 2.3 | % | Internal method |
| Flow 2 | 0.90 - 1.6 | % | Internal method |
| Transverse flow 3 | 1.0 - 1.7 | % | Internal method |
| Transverse flow 4 | 1.6 - 2.4 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.080 | % | ASTM D570 |
| Equilibrium, 23°C | 0.34 | % | ASTM D570 |
| Outdoor Suitability | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 5(Yield) | 51.7 | MPa | ASTM D638 |
| Tensile Elongation 6(Break) | 200 | % | ASTM D638 |
| Flexural Modulus 7(50.0 mm Span) | 2340 | MPa | ASTM D790 |
| Flexural Strength 8(Yield, 50.0 mm Span) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1600 | J/m | ASTM D4812 |
| Dart Drop Impact 9(23°C) | 40.7 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 154 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 54.4 | °C | ASTM D648 |
| CLTE - Flow | ASTM E831 | ||
| -40 to 40°C | 8.1E-5 | cm/cm/°C | ASTM E831 |
| 60 to 138°C | 1.4E-4 | cm/cm/°C | ASTM E831 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Oil | 23 | kV/mm | ASTM D149 |
| 3.20 mm, in Air | 16 | kV/mm | ASTM D149 |
| 3.20 mm, in Oil | 16 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 3.30 | ASTM D150 | |
| 1 MHz | 3.10 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 2.0E-3 | ASTM D150 | |
| 1 MHz | 0.020 | ASTM D150 | |
| Arc Resistance 10 | PLC 4 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 232 - 249 | °C | |
| Middle Temperature | 238 - 254 | °C | |
| Front Temperature | 243 - 260 | °C | |
| Nozzle Temperature | 238 - 254 | °C | |
| Processing (Melt) Temp | 243 - 260 | °C | |
| Mold Temperature | 49 - 77 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Vent Depth | 0.013 - 0.025 | mm |
| Note Message | |
|---|---|
| 1 . | 2.3 to 4.6 mm |
| 2 . | 0.75 to 2.3 mm |
| 3 . | 0.75 to 2.3 mm |
| 4 . | 2.3 to 4.6 mm |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | Modified |
| 10 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BX30WT6338 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| TROGAMID® CX CX9704 | Evonik Industries AG | Nylon, Unspecified | TROGAMID® CX |
| XANTAR® 27 UR | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| ESPREE™ NY613GF | SABIC Innovative Plastics | Nylon 6 | ESPREE™ |
| KEBAFLEX® SG 50 A.1 black | BARLOG plastics GmbH | TES | KEBAFLEX® |