CERTENE™ LLHC-217A
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yTLfAT_CERTENE-LLHC-217A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LLHC-217A is a certified prime grade Ethylene-Hexene copolymer for CAST Flat-Die extrusion of film applications requiring excellent clarity, high strength, toughness, low stiffness, and good tensile properties. LLHC-217A major applications include Stretch films, Diaper films and Bread films. LLHC-217A contains no slip and no antiblock. LLHC-217A complies with FDA regulation 21CFR 177.1520(c) 3.1a, and with most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 20 µm | 150 | MPa | ASTM D882 |
| 1% secant, TD : 20 µm | 170 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 9.65 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 10.3 | MPa | ASTM D882 |
| MD : Break, 20 µm | 38.6 | MPa | ASTM D882 |
| TD : Break, 20 µm | 30.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 500 | % | ASTM D882 |
| TD : Break, 20 µm | 800 | % | ASTM D882 |
| Dart Drop Impact 1(20 µm) | 95 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 280 | g | ASTM D1922 |
| TD : 20 µm | 450 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.3 µm) | 90 | ASTM D2457 | |
| Haze (20.3 µm) | 2.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen: 0.8 mils (20 µm) film; melt temperature 540-560°F (280-295°C); cast line speed 800 fpm (245 mpm). |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PS 6L5 | Witcom Engineering Plastics B.V. | PS (GPPS) | Witcom PS |
| Ultramid® SEGM35 H1 BK-126 | BASF Corporation | Nylon 6 | Ultramid® |
| HiFill® PBT/ASA GF10 BK | Techmer Engineered Solutions | PBT | HiFill® |
| KRATON® D1161 E | Kraton Polymers LLC | SIS | KRATON® |
| Sylvin 9077-70 Grey 9567 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |