Zytel® RS LC1201 BK040A
| Category: | Nylon 1010 , RENEWABLY SOURCED™ POLYAMIDES* |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® RS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ySRUUm_Zytel-RS-LC1201-BK040A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toughened, Renewably Sourced, Medium Viscosity Polyamide 1010 Developed for Extrusion |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.04 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 1.2 | -- | % | |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 108 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1500 | 930 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 45.0 | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | 30 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | > 50 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | 8.0 | kJ/m² | |
| 23°C | 16 | 25 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 9.0 | 8.0 | kJ/m² | |
| 23°C | 13 | 25 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 85.0 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 47.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 201 | -- | °C | ISO 11357-3 |
| Freezing Point 2 | 179 | -- | °C | ISO 11357 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Viscosity (250°C, 1000 sec^-1) | 215 | -- | Pa·s | ISO 11443 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC9FRN (Series: FR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Wellamid® MRGF30/10 42H-GY2 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Durez® 10694 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| GELOY™ XP4034 resin | SABIC Innovative Plastics | ASA+PC | GELOY™ |
| Karina GRAY PVC COMPOUND -E 818-18/302-CRM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |