Petrothene® NA336149 Datasheet,LDPE,LyondellBasell Industries-SHANGHAI SUSHENG

Message
Petrothene NA336 is a series of homopolymer resins selected by customers for applications that require thin gauge film constructions. NA336 resins are known for their consistency, excellent drawdown and processability.

General Information
Additive	Anti-caking agent (4000 ppm) Slip agent (1350 ppm)
Features	smoothness Homopolymer Anti-caking property Workability, good Good stripping Compliance of Food Exposure
Uses	Films Bags
Agency Ratings	FDA 21 CFR 177.1520
Forms	Particle
Processing Method	Film extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.920	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	6.5	g/10 min	ASTM D1238

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	32	µm
secant modulus			ASTM D882
1% secant, MD : 32 µm, blown film	146	MPa	ASTM D882
1% secant, TD : 32 µm, blown film	165	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Yield, 32 µm, blown film	17.2	MPa	ASTM D882
TD : Yield, 32 µm, blown film	13.9	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Broken, 32 µm, blown film	230	%	ASTM D882
TD : Broken, 32 µm, blown film	450	%	ASTM D882
Dart Drop Impact (32 µm, Blown Film)	90	g	ASTM D1709
Elmendorf Tear Strength			ASTM D1922
MD : 32 µm, blown film	350	g	ASTM D1922
TD : 32 µm, blown film	150	g	ASTM D1922

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	85.0	°C	ASTM D1525

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 31.8 µm, Blown Film)	62		ASTM D2457
Haze (31.8 µm, Blown Film)	8.0	%	ASTM D1003

Extrusion	Nominal Value	Unit
Melt Temperature	149 - 166	°C

Extrusion instructions
NA 336 has been specifically designed to provide outstanding drawdown at maximum outputs. The melt strength properties of this resin result in excellent bubble stability. This resin can be processed over a wide range of temperatures; however, recommended conditions are melt temperatures between 300°- 330°F (149°-166°C) and a blow-up ratio between 2.0-2.5:1. Using proper techniques and equipment, drawdown to 0.25 mil (6 microns) is feasible at commercial production rates.

Extrusion instructions

NA 336 has been specifically designed to provide outstanding drawdown at maximum outputs. The melt strength properties of this resin result in excellent bubble stability. This resin can be processed over a wide range of temperatures; however, recommended conditions are melt temperatures between 300°- 330°F (149°-166°C) and a blow-up ratio between 2.0-2.5:1. Using proper techniques and equipment, drawdown to 0.25 mil (6 microns) is feasible at commercial production rates.

Resin Grade	Manufacturer	Category	Trademark
NANCAR® 1072CG	Nantex Industry Co., Ltd.	NBR	NANCAR®
ALTECH® PA66 A 1000/109	ALBIS PLASTIC GmbH	Nylon 66	ALTECH® PA66
Geon™ 170 Series L140UF	Mexichem Specialty Resins, Inc.	PVC Homopolymer	Geon™ 170 Series
KumhoSunny PC HCG2510FR	Shanghai KumhoSunny Plastics Co., Ltd.	PC	KumhoSunny PC
MAJORIS DT401	AD majoris	PP, Unspecified	MAJORIS

Category:	LDPE , Low Density Polyethylene
Manufacturer:	LyondellBasell Industries
Trademark:	Petrothene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ySQf62_Petrothene-NA336149.pdf
PRICE:	Order Products email sales@su-jiao.com