Kepamid® 1330GFH
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ySP5Ya_Kepamid1330GFH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| shrinkage- Flow (3.00 mm) | 0.30 - 0.50 | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.3 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 165 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 8200 | MPa | ISO 178 |
| Flexural Stress | 230 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.80 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 90 | °C | |
| Dry Air Dryer | 80 | °C | |
| Drying Time | |||
| -- | 6.0 - 8.0 | hr | |
| Dry Air Dryer | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Hopper Temperature | 60 - 80 | °C | |
| Rear Temperature | 250 | °C | |
| Middle Temperature | 250 | °C | |
| Front Temperature | 250 | °C | |
| Nozzle Temperature | 260 | °C | |
| Mold Temperature | 70 - 90 | °C | |
| Back Pressure | 0.490 - 0.981 | MPa | |
| Screw Speed | 80 - 120 | rpm |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siloxane Masterbatch MB40-006 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| THERMOLAST® K TC5MLZ (Series: AD1) | KRAIBURG TPE | TPE | THERMOLAST® K |
| NuSil DDU-4630 | NuSil Technology | Silicone | NuSil |
| Karina WHITE PVC COMPOUND 802-10/55-AY-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom PP HU42L 205199 | LyondellBasell Industries | PP Homopolymer | Hostacom |