LNP™ LUBRICOMP™ QCL34 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ySBglO_LNPLUBRICOMPQCL34compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP QCL34 is a compound based on Nylon 6/10 resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, , Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound QCL-4034 Product reorder name: QCL34 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 17200 | MPa | ASTM D638 |
| Tensile Strength (Break) | 195 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 14100 | MPa | ASTM D790 |
| Flexural Strength | 290 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1000 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 212 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTAGLIDE PLUS | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAGLIDE |
| TIPPLEN® R 1059 A | MOL Petrochemicals Co. Ltd. | PP Random Copolymer | TIPPLEN® |
| INEOS PP 240-CA12 | INEOS Olefins & Polymers Europe | PP Random Copolymer | INEOS PP |
| LEXAN™ 123R resin | SABIC Innovative Plastics | PC | LEXAN™ |
| OP - PC/PBT 802-I | Oxford Polymers | PC+PBT | OP - PC/PBT |