Triax® 1185
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Triax® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yRnXLc_Triax-1185.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Triax 1185 resin is an ABS (Acrylonitrile Butadiene Styrene)/Nylon 6 alloy for injection molding. It is a semicrystalline thermoplastic with excellent processibility, good chemical resistance, good fatigue performance, and excellent abrasion characteristics. Triax 1185 resin has excellent impact resistance across a broad temperature range and excellent surface appearance. Triax 1185 resin is designed for use in large parts requiring a smooth finish and consistent appearance. Typical applications include components for recreational vehicles, snowmobiles, sporting goods, and a variety of parts for industrial and consumer applications. As with any product, use of Triax 1185 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 20 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 1150 | MPa | ISO 178 |
| Flexural Stress 2 | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -40°C | 28 | kJ/m² | ISO 180 |
| -30°C | 57 | kJ/m² | ISO 180 |
| 23°C | 81 | kJ/m² | ISO 180 |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C, 2.54mm, energy to peak strength | 24.0 | J | ISO 6603-2 |
| -30°C, 2.54mm, total impact penetration energy | 44.0 | J | ISO 6603-2 |
| 23°C, 2.54mm, energy to peak strength | 20.0 | J | ISO 6603-2 |
| 23°C, 2.54mm, total impact penetration energy | 40.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 52.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 190 | °C | ISO 306/A120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Shot Size | 50 - 70 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 232 - 266 | °C | |
| Middle Temperature | 232 - 266 | °C | |
| Front Temperature | 232 - 266 | °C | |
| Nozzle Temperature | 249 - 260 | °C | |
| Processing (Melt) Temp | 238 - 271 | °C | |
| Mold Temperature | 37.8 - 93.3 | °C | |
| Injection Pressure | 41.4 - 82.7 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Clamp Tonnage | 4.1 - 6.9 | kN/cm² | |
| Cushion | < 3.18 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Hold Pressure: 30 to 50% of Injection PressureScrew Speed: Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EPQ30R | Shazand (Arak) Petrochemical Corporation | PP Copolymer | Moplen |
| FHR Polypropylene AP6120-HS | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Generic ABS+Nylon - Glass Fiber | Generic | ABS+Nylon | Generic |
| PERCOM® HF FRV2 | A. Schulman Europe | PP, Unspecified | PERCOM® |
| POLYfill PPC T20040 | Polykemi AB | PP Copolymer | POLYfill |