RTP 2185 UP

Category: PEI , Polyether Imide
Manufacturer: RTP Company
Trademark: RTP
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: yRgUxB_RTP-2185-UP.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
"Warning: The status of this material is 'Commercial: Limited Issue'

The data for this material has not been recently verified.
Please contact RTP Company for current information prior to specifying this grade."
General Information
Filler / Reinforcement
  • Carbon fiber reinforced material, 30% filler by weight
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Density 1.39g/cm³ISO 1183
Moisture Content 0.040%
Additional InformationNominal ValueUnit
Primary Additive 30%
MechanicalNominal ValueUnitTest Method
Tensile Modulus (Injection Molded)28500MPaISO 527-2
Tensile Stress 240MPaISO 527-2
Tensile Strain (Yield, Injection Molded)1.5%ISO 527-2
Flexural Modulus (Injection Molded)23000MPaISO 178
Flexural Stress (Injection Molded)365MPaISO 178
ImpactNominal ValueUnitTest Method
Notched Izod Impact 1(Injection Molded)7.0kJ/m²ISO 180/1A
Unnotched Izod Impact Strength 2(Injection Molded)45kJ/m²ISO 180/1U
Additional InformationNominal ValueUnit
Data listed is for natural or black colored materials. Pigments can affect properties.Desiccant Type Dryer Required.
InjectionNominal ValueUnit
Drying Temperature - Desiccant Dryer 150°C
Drying Time - Desiccant Dryer 4.0hr
Dew Point -30.0°C
Processing (Melt) Temp 355 - 400°C
Mold Temperature 135 - 175°C
Injection Pressure 80.0 - 125MPa
Note Message
1 .4mm thickness
2 .4mm thickness
Resin Grade Manufacturer Category Trademark
UBE Nylon 7034 B UBE Engineering Plastics, S.A. Nylon 612 UBE Nylon
Bynel® 41E687 DuPont Packaging & Industrial Polymers LLDPE Bynel®
Compoceran AC156 Arakawa Chemical Industries, Ltd. Acrylic, Unspecified Compoceran
ECONAMID® 6G20FL DOMO Engineering Plastics SPA Nylon 6 ECONAMID®
Hifax TRC 134P 3004 LyondellBasell Industries PP Copolymer Hifax