Tufpet PBT G2230
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Tufpet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yRIxEn_Tufpet-PBT-G2230.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tufpet PBT G2230 is a Polybutylene Terephthalate (PBT) material filled with 30% glass fiber. It is available in North America for injection molding. Important attributes of Tufpet PBT G2230 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.72 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 1.1 | % | ASTM D955 |
| Water Absorption (Saturation, 23°C) | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 108 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 10800 | MPa | ASTM D790 |
| Flexural Strength | 162 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact | 540 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 225 | °C | |
| 1.8 MPa, Unannealed | 210 | °C | |
| RTI Elec | UL 746 | ||
| 0.740 mm | 125 | °C | |
| 1.47 mm | 125 | °C | |
| 3.05 mm | 125 | °C | |
| RTI Imp | UL 746 | ||
| 0.740 mm | 120 | °C | |
| 1.47 mm | 120 | °C | |
| 3.05 mm | 125 | °C | |
| RTI Str | UL 746 | ||
| 0.380 mm | 75.0 | °C | |
| 0.740 mm | 120 | °C | |
| 1.47 mm | 120 | °C | |
| 3.05 mm | 130 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+18 | ohms·cm | ASTM D257 |
| Dielectric Strength | 23 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.020 | ASTM D150 | |
| Arc Resistance | 125 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 300 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.380 mm | V-0 | ||
| 0.740 mm | V-0 | ||
| 1.47 mm | V-0 | ||
| 3.05 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 to 303 | °C | |
| Middle Temperature | 230 to 303 | °C | |
| Front Temperature | 230 to 303 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 81.4 | MPa | |
| Screw Speed | 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LAF471C | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Adell PP R-19 | Adell Plastics, Inc. | PP Homopolymer | Adell PP |
| Axiall PVC 9275 J Amber 05 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| TECHNYL STAR® S 218L1 V30 BLACK 1N | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |
| TECHNYL® C 216 V30 GREY 2294 | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |