SCHULATEC® PEEK NV 12
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULATEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yQT0Gb_SCHULATEC-PEEK-NV-12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| unreinforced polyetheretherketone, low viscosity |
| General Information | |
|---|---|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 36 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 102 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 10 to 20 | % | ISO 527-2/1A/50 |
| Flexural Modulus | 3900 | MPa | ISO 178 |
| Flexural Stress | 134 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 4.9 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1(1.8 MPa, Annealed) | 160 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 360 to 370 | °C | |
| Middle Temperature | 380 to 390 | °C | |
| Front Temperature | 390 to 400 | °C | |
| Nozzle Temperature | 360 to 380 | °C | |
| Processing (Melt) Temp | 390 | °C | |
| Mold Temperature | 170 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | Measured on annealed samples 3,2 mm thick, 200°C/2h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L AS310 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| NEXUS ABS ABSFR1 | Nexus Resin Group, LLC. | ABS | NEXUS ABS |
| Multi-Flex® TPE A9702 MR | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| APEX® 157V-4 | Teknor Apex Company | PVC, Flexible | APEX® |
| Huafon JF-P-8465 / JF-I-4419 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |