Silamid® L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Roonamid a.s. |
| Trademark: | Silamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yPWCbn_Silamid-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, modificated, increased impact toughness maintained even at low temperature and dry conditions, optimal processing properties, natural, other color shades according to customer's request. Suitable as a construction material where an increased impact strenght is required. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow | 1.8 | % | |
| Flow | 1.7 | % | |
| Water Absorption (23°C, 24 hr) | 1.4 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 55.0 | MPa | |
| Break | 40.0 | MPa | |
| Flexural Modulus | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 12 | kJ/m² | |
| 23°C | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 200 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4007 UP | RTP Company | PPA | RTP |
| REPOL® B250EG | Reliance Industries Limited | PP Impact Copolymer | REPOL® |
| Bio-Flex® F 1138 | FKuR Kunststoff GmbH | PLA | Bio-Flex® |
| Plaslube® PEEK CF15 TL15 A 907 BK MB | Techmer Engineered Solutions | PEEK | Plaslube® |
| XENOY™ 1102 resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |