Lotryl® 17BA07N
| Category: | EBA , Ethylene Butyl Acrylate Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Lotryl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yNscC7_Lotryl-17BA07N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LOTRYL® 17BA07N is a random copolymer of Ethylene and Butyl Acrylate produced by high-pressure radicalar polymerization process. Applications LOTRYL® 17BA07N grade thanks to the production process and the continuous quality control is polymer of choice to produce internal and external fully bonded shields for electrical cables. The process ensures unmatched polymer distribution, good carbon black dispersion, high thermal stability during extrusion and along cables use; then it extends the cable service duration. LOTRYL® 17BA07N withstand the more stringent cross-inking conditions. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.2 to 8.3 | g/10 min | ASTM D1238, ISO 1133 |
| n-Butyl Acrylate Content | 15.0 to 19.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 30 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 15.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 700 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 40.0 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 58.0 | °C | ISO 306/A, ASTM D1525 1 |
| Melting Temperature | 93.0 | °C | ISO 11357-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 to 170 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Die Temperature | 170 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 661 | RTP Company | ABS | RTP |
| reSound™ X RS1200-0215 | PolyOne Corporation | PLA Comp | reSound™ |
| KumhoSunny ASA XC230G | Shanghai KumhoSunny Plastics Co., Ltd. | ASA | KumhoSunny ASA |
| Karina WHITE PVC COMPOUND 851-10/127-Y-ERYB-AS-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ DC006ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |