SABIC® FORTIFY™ C1070D
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® FORTIFY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yMVptw_SABICFORTIFYC1070D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® FORTIFY™ C1070D is an ethylene octene copolymer produced by solution polymerization using metallocene catalyst. This product is available as free flowing pellets. SABIC® FORTIFY™ C1070D is designed as a low density and high performance copolymer modifier to provide superior impact properties and flow characteristics. Typical applications are impact modifier in thermoplastic olefin compounds, footwear midsoles and wire and cable extrusion. Please take notice of specific storage and handling conditions. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.868 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 22 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 1 sec | 71 | ASTM D2240 | |
| Shaw D, 1 sec | 21 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant | 2.90 | MPa | ASTM D638 |
| Tensile Strength (Break) | 9.30 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 850 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 13.2 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 1 | 39.2 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -52.0 | °C | Internal method |
| Melting Temperature | 62.0 | °C | Internal method |
| Additional Information |
|---|
| All physical properties were measured on compression molded specimens. |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EVAL™ E105 | Kuraray Co., Ltd. | EVOH | EVAL™ |
| Ferro PP LPP40BD24AL | Ferro Corporation | PP Homopolymer | Ferro PP |
| FREQTIS® P0833A | Polyplastics Co., Ltd. | PPS | FREQTIS® |
| Hylon® N1000EHL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| KARINTOX 70/6 | Karina Ind. e Com. de Plásticos Ltda | Polyolefin, Unspecified | KARINTOX |