| PPS 10% carbon fiber reinforced, UL 94 V0 at 1,6 mm, halogen free, surface resistivity 10^5 ohm. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | |
| Across Flow | 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 3.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 105 | °C | ASTM D648A |
| Vicat Softening Temperature | 225 | °C | ASTM D1525 1 |
| RTI Elec | 220 | °C | UL 746 |
| RTI Imp | 220 | °C | UL 746 |
| RTI Str | 220 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 320 | °C | |
| Mold Temperature | 120 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® P125 | Nilit Plastics | Nylon 66 | POLYNIL® |
| Cevian®-V T500, T500SF | Daicel Polymer Ltd. | ABS | Cevian®-V |
| Formolene® E-924 | Formosa Plastics Corporation, U.S.A. | HDPE, HMW | Formolene® |
| KOCETAL® K300EWBBK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| OTECH PVC OW620 - Cord Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |