Leona™ FR200
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yKuxcx_Leona-FR200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ FR200 is a Polyamide 66 (Nylon 66) product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Typical application: Electrical/Electronic Applications. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.16 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 1.3 to 2.0 | -- | % | Internal Method |
| Water Absorption | ||||
| Saturation, 23°C | -- | 2.4 | % | |
| Equilibrium, 23°C, 50% RH | -- | 2.4 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785, ISO 2039-2 | |||
| M-Scale | 80 | -- | ||
| R-Scale | 118 | 90 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3500 | 1100 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Yield, 23°C | 75.0 | 44.0 | MPa | ISO 527-2 |
| Break, 23°C | 69.0 | -- | MPa | ISO 527-2 |
| -- | 79.0 | 47.0 | MPa | ASTM D638 |
| Tensile Strain | ||||
| Yield, 23°C | 3.5 | 24 | % | ISO 527-2 |
| Break | 25 | 80 | % | ASTM D638 |
| Break, 23°C | 10 | > 100 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 2900 | 1100 | MPa | ASTM D790 |
| 23°C | 2900 | 1000 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 118 | 44.0 | MPa | ASTM D790 |
| 23°C | 117 | 37.2 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | -- | 8.00 | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179 | |
| Notched Izod Impact | 29 | 120 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 209 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 203 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 66.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 62.0 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 8.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | -- | J/kg/°C | |
| Thermal Conductivity | 0.20 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | ||||
| -- | 1.0E+14 | -- | ohms·cm | ASTM D257 |
| 23°C | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 19 | -- | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (3.00 mm) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 32 | -- | % | ASTM D2863 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil CV1-2289-1 | NuSil Technology | Silicone | NuSil |
| Plaslube® PA6 GF20 RM L BK | Techmer Engineered Solutions | Nylon 6 | Plaslube® |
| Resilience™ LS21150E | PolyOne Corporation | PVC, Rigid | Resilience™ |
| RTP 1499 X 139019 NAT | RTP Company | PESU | RTP |
| ULTEM™ 9075 resin | SABIC Innovative Plastics | PEI | ULTEM™ |