TECHNYL® C 536XT NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yKtlqI_TECHNYL-C-536XT-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® C 536XT Natural is an unreinforced polyamide 6, high viscosity, for extrusion blow-moulding. This product is available in natural color. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal method | |||
| Vertical flow direction | 2.1 | -- | % | Internal method |
| Flow direction | 2.1 | -- | % | Internal method |
| Water Absorption (23°C, 24 hr) | 1.3 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 1.00 | -- | Internal method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2200 | 910 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield | 54.0 | -- | MPa | ISO 527-2/1A |
| Fracture | 47.0 | 42.0 | MPa | ISO 527-2/1A |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 4.0 | -- | % | ISO 527-2/1A |
| Fracture | 55 | 190 | % | ISO 527-2/1A |
| Flexural Modulus | 1950 | 650 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 16 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 76 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact (23°C) | 66 kJ/m² | No Break | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 56.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 220 | -- | °C | ISO 11357-3 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Cylinder Zone 1 Temp. | 200 - 220 | °C | |
| Cylinder Zone 3 Temp. | 210 - 230 | °C | |
| Adapter Temperature | 210 - 230 | °C | |
| Die Temperature | 215 - 230 | °C |
| Extrusion instructions |
|---|
| Head Temperature: 220 to 230°CBlow Molding Mold Temperature: 40 to 60°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEMICOSIL® 986/1K | Wacker Chemie AG | Silicone | SEMICOSIL® |
| Karina YELLOW PVC COMPOUND TR-500D03/168-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina IVORY PVC COMPOUND 951-35/4-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLUSTEK PA4802G6BK10 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| EPITEC® NYLON-263GA | Osterman & Company | Nylon 6 | EPITEC® |