Vandar® 6000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Vandar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yKh4PF_Vandar-6000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vandar 6000 is a toughened polyester alloy with excellent cold temperature impact resistance. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.50 - 0.90 | % | ASTM D955 |
| Vertical flow direction | 0.50 - 0.90 | % | ISO 294-4 |
| Flow direction | 0.50 - 0.90 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1750 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, 23°C | 44.1 | MPa | ASTM D638 |
| Yield | 45.0 | MPa | ISO 527-2/1A/50 |
| Fracture, 23°C | 44.1 | MPa | ASTM D638 |
| 50% strain | 35.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain | |||
| Yield | 4.5 | % | ISO 527-2/1A/50 |
| Fracture, 23°C | 190 | % | ASTM D638 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 1600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Partial Break) | 56 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 106 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 70.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 74.0 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 78.0 | °C | ISO 11357-2 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 240 - 255 | °C | |
| Middle Temperature | 250 - 260 | °C | |
| Front Temperature | 250 - 260 | °C | |
| Nozzle Temperature | 260 - 270 | °C | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 65.0 - 96.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 260 to 280°CZone 4 Temperature: 255 to 265°CFeed Temperature: 240 to 255°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tefzel® HT-2160 | DuPont Fluoropolymers | ETFE | Tefzel® |
| Borealis PP WE950CF | Borealis AG | Polyolefin, Unspecified | Borealis PP |
| Laramid G/30 | LATI S.p.A. | PPA | Laramid |
| Karina IVORY PVC COMPOUND -E 751-35/ 1-C-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1105-8739/BL | Lehmann & Voss & Co. | PEEK | LUVOCOM® |